| The company selects "ChenZhou"brand antimony trioxide as the main raw material,It can solve the antimony raw material shortage supply problem by Chenzhou strong mining capacity and also the problem on surface special technique processing。Our masterbatch have edges of dust free and good distribution during performance using. As for the advantages above, more and more compounding customers are considering the masterbatch, which has relatively lower cost and dust free as well as better distribution performance. |
| Specifications of Material: |
|
1 Antimony trioxide
|
|
Antimony trioxide
|
As
|
Pb
|
Fe
|
Ni
|
Cu
|
Cd
|
Se
|
|
99.8%
|
<0.04%
|
<0.04%
|
<30ppm
|
<10ppm
|
<10ppm
|
<5ppm
|
<10ppm
|
|
Hg
|
Particle size
|
Color
|
L
|
a
|
b
|
Black Spot
|
50µm sieve
|
|
<10ppm
|
0.6-1.2 µm
|
white
|
>94
|
(-0.5,+0.5)
|
1.5-2.5
|
≤10
|
≤0.008%
|
|
PBT resin :Taiwan Changchun: PBT/1200-211 M
|
|
Specific Gravity
|
Melt flow rate
|
shrinkage
|
Water absorption
|
Rockwell Hardness
|
Tensile stress
|
Tensile strain
|
|
1.31g/cm3
|
46g/10min
|
0.12-0.18%
|
0.60%
|
87
|
55.0MPa
|
>50%
|
|
Bending modulus
|
Bending strength
|
Thermal deformation temperature
|
Melting temperature
|
Linear expansion coefficient
|
Surface resistivity
|
Dielectric strength
|
|
2450MPa
|
83MPa
|
155℃
|
223-227℃
|
0.000090cm/cm/℃
|
1.0E+13ohms
|
20V/mm
|
|
| Specifications of Finished product: |
|
Model
|
Appearance
|
SB2O3
|
Carrier and auxiliary
|
Melting point
|
Main carrier
|
Size
|
|
CZG-70B
|
white granules
|
70±1%
|
≤30%
|
225℃
|
PBT
|
2mm-4mm
|
|
CZG-80B
|
white granules
|
80±1%
|
≤20%
|
225℃
|
PBT
|
2mm-4mm
|
|
| Features: |
a. No dust pollution, So workers will not skin allergy or other occupational disease. b . Measures up the requirement of RoHS, REACH, PAHs and other environmental protection standard c. It has good compatibility with resin, distribution performance is good, good fluidity, high thermal stability. d. It plays a role of coordinated effect with all kinds of flame retardants. e. Non-loss, reduce the dosage of antimony trioxide, effectively save resources.
|
| Uses: |
used for PBT, PA as flam retardant, produce after mix with base resin and additives.
|
| Packing: |
25KG/bag, 1MT/bag, PE bag lined paper-plastic laminated film bag.
|